Search found 182 matches

by Slipshine
Mon Jun 27, 2016 1:32 am
Forum: Filament
Topic: eSun PLA+ filament
Replies: 38
Views: 21877

Re: eSun PLA+ filament

That figures. I guess I should have waited. I think the other roll says pla+ maybe Ill give it a try even though Its the wrong color for my project. I will say it seems strong and flexible. Just hate dialing in a profile for one roll I can never get again. Im beginning to loose faith in esun. May ha...
by Slipshine
Sun Jun 26, 2016 5:56 pm
Forum: Filament
Topic: eSun PLA+ filament
Replies: 38
Views: 21877

Re: eSun PLA+ filament

I ordered a couple rolls of this awile back and just started using it today. So far not alot of luck. Did anyone else have problems with it wanting to bind in the ptfe tube. It is not oversized but it comes off the roll very wavy and that causes it to fit tight in the tube. Also the black roll im us...
by Slipshine
Sun Jun 26, 2016 4:47 pm
Forum: Printed Object Showcase
Topic: Hydrogen Generator
Replies: 88
Views: 22461

Re: Hydrogen Generator

I have really enjoyed following this project. I would like to thank you for taking the time to share this incredible build.

I was wondering how much pressure can the system generate before its a problem .

Also is there an effective way to compress and store for later use.

Thanks.
by Slipshine
Sun Jun 26, 2016 4:30 pm
Forum: Getting Started
Topic: Higher definition, higher warp?
Replies: 3
Views: 2630

Re: Higher definition, higher warp?

1. The thinner you print the less tolerant overhangs will be. 2. On your first layer settings when printing at .100 Set your first layer height to 200%. That being said you can try printing at a slightly lower temp it will help some. .100 is a bit tricky. You may want to try at .150 layer height . I...
by Slipshine
Tue Jun 21, 2016 6:54 pm
Forum: Printed Object Showcase
Topic: Hydrogen Generator
Replies: 88
Views: 22461

Re: Hydrogen Generator

Shades of the NSA stopping by....

Honey did one of the neighborhood kids get a new drone???
by Slipshine
Tue Jun 21, 2016 3:29 pm
Forum: Tech Support
Topic: PETG Infill Rot
Replies: 35
Views: 8102

Re: PETG Infill Rot

What thickness of MIC6 are you using? It looks like you don't see the high tolerances on levelness until you get to 3/4" or thicker. At 1/4" I'm seeing .015" tolerance, which is no better than glass. . I have a tendency to agree with this. My mic 6 plate is .012 inches out on one side fortunately t...
by Slipshine
Tue Jun 14, 2016 11:47 pm
Forum: Other (off topic)
Topic: slidoodle (closed)
Replies: 6
Views: 5681

Re: slidoodle (closed)

I thought I had read that he had worked for Makergear in his Bio when he first started up.

Hope he lands on his feet. Seems like a decent guy just overstepped his position.
by Slipshine
Thu Jun 09, 2016 9:38 pm
Forum: Filament
Topic: 3DXTech Carbon fiber infused abs
Replies: 18
Views: 8081

Re: 3DXTech Carbon fiber infused abs

what bed prep are you using while printing with this stuff?
by Slipshine
Wed Jun 08, 2016 1:05 pm
Forum: Printed Object Showcase
Topic: Hydrogen Generator
Replies: 88
Views: 22461

Re: Hydrogen Generator

Wishing you the best.
by Slipshine
Sat Jun 04, 2016 10:51 pm
Forum: Other (off topic)
Topic: slidoodle (closed)
Replies: 6
Views: 5681

slidoodle (closed)

FYI I just found out that Solidoodle whent under. For those that don't know they made a low end printer that was pretty popular. According to their blog they tried to come out with a 5th version of there machine made entirely in china and it ended up bankrupting the company. Guess they should have s...