awesome! thanks Jules. I was expecting the option to be within the profile editor!

I exported my print profiles from the previous version but it doesnt seen to have a method for importing them into version 3.

Am I blind?

Am I correct in assuming that if I use a good adhesive that having a perfectly clean bed isnt as critical? will hairspray release once the bed is cold or do you have to fight the parts off?

it looks like my assumption that the tension on the extruder had to be higher to grip the flexible stuff was a big part of the problem here, I backed it off entirely and it feeds well at SLOW speeds. I had already had it at 30mm/sec but dropped it to 25 to see if that would improve it, I settled bac...

insta, when you say all other speeds to 100% what should me default speed be? is 1500mm/min good ?

This stuff is brutal to use. I managed to get it to print the calibration box, albeit not that great. Once that was done I tried a full print and it jammed, I cleared the jam, extruded some filament, began the print again, JAMMED again. If anyone can tell me that ninjaflex is easier to print with I ...

excellent advice Jim! now how would I go about adjusting the jog speed? and the only filament I have printed with is PLA, actually only the PLA that came with the printer so far. I have a freshly cleaned hot end, should I just dedicate that for flex and be done with it?? EDIT: right after I asked ho...

I havent actually tried printing, just purging the PLA from the nozzle it was going great then started to slow and bind.

the printing temps for this are listed as the same for their PLA so I tried using my PLA temps and it just wont stop binding in my extruder. I've tried going all the way up to 250C and pushing it through by hand but it has a TON of resistance. when I first warm it up it goes through eagerly and then...

I have set up a thingiverse account, the Dial clamp and a few other things I've made are there, my username is Farr0wn3d

if you have any positive or constructive feedback I'd love to hear it.